Dentin wetting by four adhesive systems.

J I Rosales-Leal·R Osorio·J A Holgado-Terriza·M A Cabrerizo-Vílchez·M Toledano
View original source ↗Export metadata ↓

Abstract

OBJECTIVES: To evaluate the dentin wetting by four adhesive systems and to relate the wetting properties with the adhesive efficiency. METHODS: Scotch Bond Multipurpose Plus (3M), Syntac Single-Component (Vivadent), One-Step (Bisco) and Heliobond (Vivadent) were used. The substrate was superficial and deep human dentin. Roughness and water contact angle were measured before and after acid etching. Dentin wetting by resins was studied by contact angle measurements as a function of time to evaluate the spreading time. The shear bond strength was evaluated following a single plane method, and the microleakage was evaluated in Class V cavities. RESULTS: Acid etching increased dentin roughness and wettability and no differences were found between acids tested. Dentin wetting and roughness was higher on deep dentin. Dentin wetting and shear bond strength of resins was similar except for Heliobond that displayed the lowest value. Microleakage was higher on the gingival wall, and the leaking was lowest for Scotch Bond Multipurpose Plus, and maximum for Heliobond. The spreading time exceeded 30s with water-based and hydrophobic adhesives, and was lower with an acetone-based adhesive. Dentin depth had some influence on contact angle and shear bond strength: contact angles obtained with SBMP and One-Step were higher on superficial dentin, and shear bond strength for One-Step was higher on superficial dentin. Dentin wetting by resins could be correlated to shear bond strength and microleakage. SIGNIFICANCE: Dentin acid etching with different conditioners promotes similar roughness and wetting changes. On a similar substrate, the adhesion depends on the chemical and wetting characteristics of resins.

Explore related subjects

Acid Etching, DentalAcrylatesAdhesivenessAnalysis of VarianceDental BondingDental LeakageDentinDentin-Bonding AgentsHumansMaterials TestingMethacrylatesMolarResin CementsStatistics, NonparametricSurface PropertiesTensile StrengthWettabilityComparative StudyJournal ArticleResearch Support, Non-U.S. Gov't

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

J I Rosales-Leal, R Osorio, J A Holgado-Terriza, M A Cabrerizo-Vílchez, M Toledano. 2001. Dentin wetting by four adhesive systems.. https://doi.org/10.1016/s0109-5641(01)00014-8

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2007

Resin strengthening of dental ceramics- the impact of surface texture and silane.

OBJECTIVES: To examine the effect of porcelain surface texture achieved utilising three clinically relevant surface preparation methods prior to silane and unfilled resin application on the flexure strength of a low fusing feldspathic porcelain. MATERIALS AND METHODS: Five hundred and forty dentine disc-shaped specimens (15.0mm diameter and 0.9mm thickness) were condensed, fired and allocated to 18 groups. Six groups were stored as-fired, six were alumina abraded and six were acid-etched. Samples were coated with silane, unfilled resin or both prior to bi-axial flexure testing. Group means were compared utilising a three factor design general linear model and post hoc all paired Tukey tests at P<0.05. Weibull analysis was employed to examine the reliability of the strength data. Profilometry was used to characterise the surface texture of the specimen surfaces. RESULTS: Alumina abraded and acid-etched specimens had significantly lower flexure strengths than the as-fired specimens. A significant difference between the degree of strengthening observed following unfilled resin application on the three surface texture investigated was observed (P<0.001). Silane application prior to resin coating resulted in no further significant increases in the mean bi-axial flexure strengths of the three surface textures. The as-fired surfaces had a low frequency of irregular amplitude defects, alumina abraded surfaces had an increased frequency of regular amplitude defects whilst the acid-etched surface consisted of an increased frequency of irregular amplitude defects. CONCLUSION: The strengthening mechanism whilst dependent on surface texture was independent of defect severity. No significant strengthening occurred following silane priming suggesting that, for the unfilled resin utilised, the strengthening mechanism was not enhanced by improved resin-ceramic adhesion.

Acid Etching, Dental↗
PubMed2007

Effect of different types of enamel conditioners on the bond strength of orthodontic brackets.

AIM: A unique characteristic of some new bonding systems in operative dentistry is they combine conditioning and priming agents into a single acidic primer solution for simultaneous use on both enamel and dentin. Combining conditioning and priming into a single treatment step results in improvement in both time and cost-effectiveness to the clinician and, indirectly, to the patient. The purpose of this study was to determine the effects of the use of a self-etching primer on the bond strength of orthodontic brackets and on the bracket/adhesive failure mode. METHODS AND MATERIALS: Thirty-six fresh bovine incisors were collected and stored in a solution of 0.1% (weight/volume) thymol. The criteria for tooth selection included intact buccal enamel, no cracks caused by the presence of the extraction forceps, and no defects. The teeth were cleansed and polished with pumice and rubber prophylactic cups for ten seconds. Brackets were bonded to the teeth according to one of three protocols following the manufacturers' instructions--Group 1: Conventional multistep bonding system (control group) (n=12); Group 2: Self-etching primer system (n=12); and Group 3: Acid+self-etching primer system (n=12). Specimens were loaded to failure in a Zwick test machine (Zwick GmbH & Co, Ulm, Germany). Shear bond strengths were measured at a crosshead speed of 5 mm/min. RESULTS: The mean shear bond strength in megapascals (Mpa) (standard deviation) were 11.7 (4.2), 10.5 (4.4), and 10.9 (4.8) for Groups 1, 2, and 3, respectively. The analysis of variance (ANOVA) was used to compare the three groups. The results indicated no significant difference in the bond strength between the three groups (P=0.800). The results of the Chi square test, evaluating the residual adhesives on the enamel surfaces, revealed no significant difference between the three groups (P=0.554). CONCLUSION: Results of the present in vitro study indicate the use of self-etching primers may be an alternative to conventional phosphoric acid pre-treatment in orthodontic bonding.

Acid Etching, Dental↗
PubMed2007

Removal of noncollagenous components affects dentin bonding.

The structural integrity of fibrillar type I collagen is critical for effective dentin bonding. Since most noncollagenous matrix components in dentin are closely associated with collagen, we hypothesized that they may also contribute to dentin bonding. To test this hypothesis, bovine dentin was acid-etched, treated with chondroitinase ABC (C-ABC), endo-beta-galactosidase (Endo-beta), or trypsin. Controls were prepared in the same manner but without the enzymes. All control and experimental specimens were then bonded with One-Step. Bond strength data were analyzed by one-way ANOVA and Fisher's PLSD test (p < 0.05). When dentin was treated with C-ABC or trypsin, bond strengths significantly decreased for the rewetted groups (p < 0.05). The treatment with Endo-beta showed no effects on bond strengths (p > 0.05). When the treated dentin surfaces were observed under SEM, the C-ABC and trypsin treated groups revealed significant loss of collagen fibril architecture. The results indicate that chondroitin sulfate glycosaminoglycans and trypsin-digestible noncollagenous proteins play roles in maintaining the open dimensions of the collagen fibril scaffold, which is essential for optimal dentin bonding.

Acid Etching, Dental↗