Does excessive occlusal load affect osseointegration? An experimental study in the dog.

L J Heitz-Mayfield·B Schmid·C Weigel·S Gerber·D D Bosshardt·J Jönsson·N P Lang
View original source ↗Export metadata ↓

Abstract

AIM: The purpose of this study was to evaluate the effect of excessive occlusal load following placement of titanium implants in the presence of healthy peri-implant mucosal tissues. MATERIALS AND METHODS: Mandibular bilateral recipient sites in six Labrador dogs were established by extracting premolars and molars. After 3 months, two TPS (titanium plasma sprayed) implants and two SLA (sandblasted, large grit, acid etched) implants were placed on each side of the mandible in each dog. Three implants were lost in the initial healing phase, leaving 45 implants for evaluation. Following 6 months of healing, gold crowns were placed on implants on the test side of the mandible. The crowns were in supra-occlusal contact with the opposing teeth in order to create excessive occlusal load. Implants on the control side were not loaded. Plaque control was performed throughout the experimental period. Clinical measurements and standardised radiographs were obtained at baseline and 1, 3 and 8 months after loading. At 8 months, the dogs were killed and histologic analyses were performed. RESULTS: At 8 months, all implants were osseointegrated. The mean probing depth was 2.5+/-0.3 and 2.6+/-0.3 mm at unloaded and loaded implants, respectively. Radiographically, the mean distance from the implant shoulder to the marginal bone level was 3.6+/-0.4 mm in the control group and 3.7+/-0.2 mm in the test group. Control and test groups were compared using paired non-parametric analyses. There were no statistically significant changes for any of the parameters from baseline to 8 months in the loaded and unloaded implants. Histologic evaluation showed a mean mineralised bone-to-implant contact of 73% in the control implants and 74% in the test implants, with no statistically significant difference between test and control implants. CONCLUSION: In the presence of peri-implant mucosal health, a period of 8 months of excessive occlusal load on titanium implants did not result in loss of osseointegration or marginal bone loss when compared with non-loaded implants.

Explore related subjects

Acid Etching, DentalAir Abrasion, DentalAlveolar Bone LossAlveolar ProcessAnimalsBite ForceCoated Materials, BiocompatibleCrownsDental ImplantsDental Prosthesis DesignDental Prosthesis, Implant-SupportedDogsMandibleModels, AnimalOsseointegrationPeriodontal PocketRadiographyTime FactorsTitaniumWound HealingComparative StudyJournal ArticleResearch Support, Non-U.S. Gov't

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

L J Heitz-Mayfield, B Schmid, C Weigel, S Gerber, D D Bosshardt, J Jönsson, N P Lang. 2004. Does excessive occlusal load affect osseointegration? An experimental study in the dog.. https://doi.org/10.1111/j.1600-0501.2004.01019.x

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related citations

PubMed2007

Resin strengthening of dental ceramics- the impact of surface texture and silane.

OBJECTIVES: To examine the effect of porcelain surface texture achieved utilising three clinically relevant surface preparation methods prior to silane and unfilled resin application on the flexure strength of a low fusing feldspathic porcelain. MATERIALS AND METHODS: Five hundred and forty dentine disc-shaped specimens (15.0mm diameter and 0.9mm thickness) were condensed, fired and allocated to 18 groups. Six groups were stored as-fired, six were alumina abraded and six were acid-etched. Samples were coated with silane, unfilled resin or both prior to bi-axial flexure testing. Group means were compared utilising a three factor design general linear model and post hoc all paired Tukey tests at P<0.05. Weibull analysis was employed to examine the reliability of the strength data. Profilometry was used to characterise the surface texture of the specimen surfaces. RESULTS: Alumina abraded and acid-etched specimens had significantly lower flexure strengths than the as-fired specimens. A significant difference between the degree of strengthening observed following unfilled resin application on the three surface texture investigated was observed (P<0.001). Silane application prior to resin coating resulted in no further significant increases in the mean bi-axial flexure strengths of the three surface textures. The as-fired surfaces had a low frequency of irregular amplitude defects, alumina abraded surfaces had an increased frequency of regular amplitude defects whilst the acid-etched surface consisted of an increased frequency of irregular amplitude defects. CONCLUSION: The strengthening mechanism whilst dependent on surface texture was independent of defect severity. No significant strengthening occurred following silane priming suggesting that, for the unfilled resin utilised, the strengthening mechanism was not enhanced by improved resin-ceramic adhesion.

Acid Etching, Dental↗
PubMed2007

Effect of different types of enamel conditioners on the bond strength of orthodontic brackets.

AIM: A unique characteristic of some new bonding systems in operative dentistry is they combine conditioning and priming agents into a single acidic primer solution for simultaneous use on both enamel and dentin. Combining conditioning and priming into a single treatment step results in improvement in both time and cost-effectiveness to the clinician and, indirectly, to the patient. The purpose of this study was to determine the effects of the use of a self-etching primer on the bond strength of orthodontic brackets and on the bracket/adhesive failure mode. METHODS AND MATERIALS: Thirty-six fresh bovine incisors were collected and stored in a solution of 0.1% (weight/volume) thymol. The criteria for tooth selection included intact buccal enamel, no cracks caused by the presence of the extraction forceps, and no defects. The teeth were cleansed and polished with pumice and rubber prophylactic cups for ten seconds. Brackets were bonded to the teeth according to one of three protocols following the manufacturers' instructions--Group 1: Conventional multistep bonding system (control group) (n=12); Group 2: Self-etching primer system (n=12); and Group 3: Acid+self-etching primer system (n=12). Specimens were loaded to failure in a Zwick test machine (Zwick GmbH & Co, Ulm, Germany). Shear bond strengths were measured at a crosshead speed of 5 mm/min. RESULTS: The mean shear bond strength in megapascals (Mpa) (standard deviation) were 11.7 (4.2), 10.5 (4.4), and 10.9 (4.8) for Groups 1, 2, and 3, respectively. The analysis of variance (ANOVA) was used to compare the three groups. The results indicated no significant difference in the bond strength between the three groups (P=0.800). The results of the Chi square test, evaluating the residual adhesives on the enamel surfaces, revealed no significant difference between the three groups (P=0.554). CONCLUSION: Results of the present in vitro study indicate the use of self-etching primers may be an alternative to conventional phosphoric acid pre-treatment in orthodontic bonding.

Acid Etching, Dental↗
PubMed2007

Removal of noncollagenous components affects dentin bonding.

The structural integrity of fibrillar type I collagen is critical for effective dentin bonding. Since most noncollagenous matrix components in dentin are closely associated with collagen, we hypothesized that they may also contribute to dentin bonding. To test this hypothesis, bovine dentin was acid-etched, treated with chondroitinase ABC (C-ABC), endo-beta-galactosidase (Endo-beta), or trypsin. Controls were prepared in the same manner but without the enzymes. All control and experimental specimens were then bonded with One-Step. Bond strength data were analyzed by one-way ANOVA and Fisher's PLSD test (p < 0.05). When dentin was treated with C-ABC or trypsin, bond strengths significantly decreased for the rewetted groups (p < 0.05). The treatment with Endo-beta showed no effects on bond strengths (p > 0.05). When the treated dentin surfaces were observed under SEM, the C-ABC and trypsin treated groups revealed significant loss of collagen fibril architecture. The results indicate that chondroitin sulfate glycosaminoglycans and trypsin-digestible noncollagenous proteins play roles in maintaining the open dimensions of the collagen fibril scaffold, which is essential for optimal dentin bonding.

Acid Etching, Dental↗